Tribocorrosion behaviour of electroless Ni–P coating on AA7075 aluminum alloy

---

Atıf İçin Kopyala

MİNDİVAN H.

Acta Physica Polonica A, cilt.135, sa.5, ss.1103-1106, 2019 (SCI-Expanded)

• Yayın Türü: Makale / Tam Makale
• Cilt numarası: 135 Sayı: 5
• Basım Tarihi: 2019
• Doi Numarası: 10.12693/aphyspola.135.1102
• Dergi Adı: Acta Physica Polonica A
• Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
• Sayfa Sayıları: ss.1103-1106
• Açık Arşiv Koleksiyonu: AVESİS Açık Erişim Koleksiyonu
• Bilecik Şeyh Edebali Üniversitesi Adresli: Evet

Özet

© 2019 Polish Academy of Sciences. All rights reserved.Electroless Ni–P coating was deposited on an AA7075 aluminum (Al) alloy, and its morphology, microhardness and tribocorrosion behaviour were evaluated. Coating characterization was done using light optic microscope (LOM) and field emission gun scanning electron microscope (FEG-SEM). Tribocorrosion tests were performed under open circuit potential (OCP) using a reciprocating ball-on-plate tribometer where a 10 mm diameter alumina ball was used as counter material and a normal load of 10 N was applied during 45 min. The Ni–P coating’s microhardness and tribocorrosion performance were higher than untreated alloy.