Tribological behavior of αı/βı-SiAlON-TiN composites
Journal of the European Ceramic Society, cilt.38, sa.5, ss.2279-2288, 2018 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 38 Sayı: 5
- Basım Tarihi: 2018
- Doi Numarası: 10.1016/j.jeurceramsoc.2018.01.013
- Dergi Adı: Journal of the European Ceramic Society
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Sayfa Sayıları: ss.2279-2288
- Anahtar Kelimeler: Cutting tool, Microstructure, Tribology, Wear mechanisms, αı:βı-SiAlON-TiN composites
- Bilecik Şeyh Edebali Üniversitesi Adresli: Evet
Özet
© 2018 Elsevier LtdThere are limited studies on the tribological properties of SiAlON-TiN composites. Therefore, in the present study, tribology tests were conducted on a number of αı/βı-SiAlON-TiN composites with different αı/βı-SiAlON phase ratio and TiN content, fabricated with unique compositional design. The influence of αı/βı-SiAlON phase ratios, microstructure, mechanical properties and TiN content on friction and wear behavior was investigated and wear mechanisms were explained. Tribology tests were conducted on computer controlled tribometer under dry unlubricated ambient conditions with a linear reciprocating movement in a ball-on-disc sliding wear configuration and test parameters kept as constant. It was observed that TiN addition (17 wt.%) did not change the friction (CoF) of SiAlON and wear rate and wear volume were observed to increase. Wear mechanisms showed differences with αı:βı-SiAlON phase ratio. Fracture toughness had very pronounced effect on wear resistance.