Engineering Features of Dung Ash Substituted Cement Mortars

Creative Commons License

ALTUNCI Y. T., ÖCAL C.

Bilecik Şeyh Edebali Üniversitesi Fen Bilimleri Dergisi, vol.8, no.1, pp.24-31, 2021 (Peer-Reviewed Journal)

Abstract

In this study, engineering features of dung ash substituted cement mortars were investigated. Cow dung materialwas calcined at 400 °C and turned into dung ash, and the mixtures were prepared by substituting 0%, 2%, 4%,6%, 8%, and 10% by weight instead of CEM I 42.5 R type cement. Setting times, expansions, spreadingdiameters, unit weight and bending, and compressive strengths of 2 and 28 days of prepared mixtures weredetermined. As a result, with the increase in the rate of substitution; it was determined that setting times werelonger, spreading diameters, unit weight, bending, and compressive strengths decreased. In addition, it wasdetermined that the substitution of dung ash up to 8% by weight instead of Portland cement did not affect theperformance negatively in terms of the experiments.
Bu çalışmada tezek külü ikameli çimento harçlarının mühendislik özellikleri incelenmiştir. İnekten elde edilentezek malzemesi 400 0C de kalsine edilerek tezek külü haline getirilmiş ve CEM I 42.5 R tipi çimento yerineağırlıkça %0, %2, %4, %6, %8 ve %10 oranlarında ikame edilerek karışımlar hazırlanmıştır. Hazırlanankarışımların; priz süreleri, genleşmeleri, yayılma çapları, birim hacim ağırlıkları ile 2 ve 28 günlük eğilme vebasınç dayanımları belirlenmiştir. Sonuç olarak ikame oranı artışı ile priz sürelerinin uzadığı, yayılma çaplarının,birim hacim ağırlıklarının, eğilme ve basınç dayanımlarının azaldığı belirlenmiştir. Ayrıca tezek külününportland çimentosu yerine ağırlıkça %8 oranına kadar ikame edilmesinin yapılan deneyler açısından performansıolumsuz etkilemediği belirlenmiştir.