A comparative characterization of the HPA-MCM-48 type catalysts produced by the direct hydrothermal and room temperature synthesis methods


Creative Commons License

Gucbilmez Y., YARGIÇ A. Ş., Calis I.

Journal of Nanomaterials, vol.2012, 2012 (SCI-Expanded) identifier

  • Publication Type: Article / Article
  • Volume: 2012
  • Publication Date: 2012
  • Doi Number: 10.1155/2012/210437
  • Journal Name: Journal of Nanomaterials
  • Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Bilecik Şeyh Edebali University Affiliated: Yes

Abstract

MCM-48 type support materials synthesized by the direct hydrothermal synthesis (HTS) and room temperature synthesis (RTS) methods were incorporated with tungstophosphoric acid (TPA) in the range of 10-40wt by using a wet impregnation technique in methanol solutions. Resulting HPA-MCM-48 catalysts were characterized by the XRD, Nitrogen Physisorption, SEM, TEM, EDS, and FT-IR methods in order to determine the effects of different initial synthesis conditions on the catalyst properties. RTS samples were found to have better crystalline structures, higher BET surface areas, and higher BJH pore volumes than HTS samples. They also had slightly higher TPA incorporation, except for the 40wt samples, as evidenced by the EDS results. Keggin ion structure was preserved, for both methods, even at the highest acid loading of 40wt. It was concluded that the simpler and more economical RTS method was more successful than the HTS method for heteropoly acid incorporation into MCM-48 type materials. © 2012 Y. Gucbilmez et al.