B4C particle-reinforced al matrix composites production from 7075 al alloy chips by hot pressing


Meydanoglu O., MİNDİVAN H., Çimenoğlu H., Sabri Kayali E.

TMS 2007 Annual Meeting and Exhibition, Orlando, FL, Amerika Birleşik Devletleri, 25 Şubat - 01 Mart 2007, ss.1167-1170 identifier

  • Yayın Türü: Bildiri / Tam Metin Bildiri
  • Basıldığı Şehir: Orlando, FL
  • Basıldığı Ülke: Amerika Birleşik Devletleri
  • Sayfa Sayıları: ss.1167-1170
  • Anahtar Kelimeler: Aluminum, B4C, Metal matrix composite, Wear
  • Bilecik Şeyh Edebali Üniversitesi Adresli: Hayır

Özet

In this study, producibility of B4C particle reinforced Al alloy matrix composites from 7075 Al alloy machining chips has been investigated. After blending 7075 Al alloy with 10 wt % B4C particles, mixtures were pressed at 350°C for two hours under a pressure of 625 MPa. Characterization of the composites was made by structural examinations and mechanical tests (hardness and dry sliding wear tests). When compared to conventionally extruded 7075 Al alloy, 10 wt.% B4C particles reinforced 7075 aluminum alloy matrix composite exhibited superior hardness and wear resistance especially after T6 tempering.