Super alloys are widely used in the field of aviation and they are difficult to machine. Alumina and silicon nitride based ceramic matrix composites have been used for super alloy machining. Since SiAlON based ceramic cutting tools can be produced with gas pressure sintering method which is suitable for serial production, they provide cost advantages over Al2O3-SiCw cutting tools. However SiAlON ceramics have the disadvantage for super alloy machining due to inadequate properties in respect of chemical durability. Therefore in this study in order to enhance chemical durability of SiAlON ceramics, SiAlON based ceramics prepared with unique compositional design with TiN incorporation. SiAlON-TiN composites were prepared in pilot scale which allows description of the problems and their solutions. The optimization efforts in the production process of SiAlON-TiN cutting tools with the desired properties have been achieved in a pilot scale.
Süper alaşımlar havacılık alanında yaygın olarak kullanılan ve işlenmesi zormalzemelerdir. Alümina ve silisyum nitrür esaslı seramik matrisli kompozitlersüper alaşımların işlenmesinde kullanılmaktadırlar. SiAlON esaslı seramik kesiciuçlar seri üretime uygun gaz basınçlı sinterleme tekniği ile üretilebildikleri içinAl2O3-SiCw kesici uçlara karşı maliyet avantajı sağlamaktadırlar. Ancak SiAlONseramikleri kimyasal dayanım açısından süper alaşım işlenmesinde yeterli değildir.Bu nedenle bu çalışmada SiAlON seramiklerinin kimyasal dayanımını arttırmak içinTiN ilavesi yapılarak özgün kompozisyon tasarımlarıyla hazırlanmış SiAlON-TiNkompozitlerinin pilot ölçekte üretimi yapılarak, üretim esnasında karşılaşılansorunlar ve çözüm önerileri açıklanmıştır. Üretim sürecinde yapılan optimizasyonçalışmaları neticesinde istenen özelliklerde kesici uç üretimi pilot ölçektebaşarılmıştır.